NO | CHARACTERISTIC | RESULT | ACCEPTED LIMIT | METHOD |
1 | Kinematic viscosity at 100 ˚C | 5.8 cSt | 4.5-6 cSt | ASTM D-445 |
2 | Congealing Point | 55.5 ˚C | 50-54 ˚C | ASTM D-938 |
3 | Penetration Consistency | 137 (0.1 mm) | 130-150 (0.1 mm) | ASTM D-937 |
4 | Color (Lovibond) | 1.1 Y | Max 1.1 Y | IP-17 Method A 2 cell |
5 | Acidity or Alkalinity | Passed | According to test method | B.P 2007 |
6 | Polycyclic aromatic Hydrocarbons | Passed | Not more than absorbance of solution 6 mg/l Naphthalene in DMSO@278 nm | B.P 2007 |
7 | Light Absorbance 0.05% w/v in trimethyl pentane 290 nm | 0.13 | Not more than 0.5 | B.P 2007 |
8 | Odor | Passed | Odorless when rubbed on hand | ——- |
NO | CHARACTERISTIC | RESULT | ACCEPTED LIMIT | METHOD |
1 | Kinematic viscosity at 100 ˚C | 5.8 cSt | 4.5-6 cSt | ASTM D-445 |
2 | Congealing Point | 55.5 ˚C | 50-54 ˚C | ASTM D-938 |
3 | Penetration Consistency | 137 (0.1 mm) | 130-150 (0.1 mm) | ASTM D-937 |
4 | Color (Lovibond) | 1.1 Y | Max 1.1 Y | IP-17 Method A 2 cell |
5 | Acidity or Alkalinity | Passed | According to test method | B.P 2007 |
6 | Polycyclic aromatic Hydrocarbons | Passed | Not more than absorbance of solution 6 mg/l Naphthalene in DMSO@278 nm | B.P 2007 |
7 | Light Absorbance 0.05% w/v in trimethyl pentane 290 nm | 0.13 | Not more than 0.5 | B.P 2007 |
8 | Odor | Passed | Odorless when rubbed on hand | ——- |