NO. | CHARACTERISTIC | RESULT | ACCEPTED LIMIT | METHOD |
1 | Kinematic viscosity at 100 ˚C | 6.1 cSt | 6-8 cSt | ASTM D-445 |
2 | Congealing Point | 57 ˚C | 45-58 ˚C | ASTM D-938 |
3 | Penetration Consistency | 157 (0.1 mm) | 140-160 (0.1 mm) | ASTM D-937 |
4 | Color (Lovibond) | 0.2 Y | Max 0.5 Y | IP-17 Method A 2 cell |
5 | Acidity or Alkalinity | Passed | According to test method | B.P 2007 |
6 | Odor | Passed | Odorless when rubbed on hand | ——- |
7 | Polycyclic aromatic Hydrocarbons | Passed | Not more than absorbance of solution 6mg/l Naphthalene in DMSO @ 278 nm | B.P 2007 |
NO. | CHARACTERISTIC | RESULT | ACCEPTED LIMIT | METHOD |
1 | Kinematic viscosity at 100 ˚C | 6.1 cSt | 6-8 cSt | ASTM D-445 |
2 | Congealing Point | 57 ˚C | 45-58 ˚C | ASTM D-938 |
3 | Penetration Consistency | 157 (0.1 mm) | 140-160 (0.1 mm) | ASTM D-937 |
4 | Color (Lovibond) | 0.2 Y | Max 0.5 Y | IP-17 Method A 2 cell |
5 | Acidity or Alkalinity | Passed | According to test method | B.P 2007 |
6 | Odor | Passed | Odorless when rubbed on hand | ——- |
7 | Polycyclic aromatic Hydrocarbons | Passed | Not more than absorbance of solution 6mg/l Naphthalene in DMSO @ 278 nm | B.P 2007 |